Graphite carbon Mould Used to Make Cell Phone Glass Screen curved glass Flexible glass
Propety | Isostatic Gaphite | Molded Gaphite | 0.8mm | Unit | |||||
XRD-7W | XRD-8W | XRD-10J | XRD-40B | XRD-50B | XRD-40D | XRD-50D | XRD-8D | ||
Bulk Density | 1.85 | 1.91 | 1.85 | 1.78 | 1.84 | 1.68 | 1.78 | 1.72 | g/cm3 |
Resistivity | 11~13 | 11~13 | 16.5 | 7~12 | 7~12 | 12~16 | 12~16 | 9 | μ.m |
Thermal Conductivity | 85 | 85 | 119.5 | * | * | * | * | * | W/m.k |
C.T.E. | 5.6 | 5.85 | 5.89 | * | * | * | * | * | 10-6/℃ |
Shore Hardness | 65 | 70 | 73 | 42 | 50 | 50 | 55 | * | HSD |
Flexural Strength | 51 | 60 | 70 | 38 | 45 | 40 | 45 | 13 | Mpa |
Compression Strength | 115 | 135 | 140 | 72 | 90 | 82 | 88 | 32 | Mpa |
Porosity | 12 | 11 | 12 | 17 | 13 | 18 | 13 | * | % |
Ash content | 50 | 10 | 40 | 900 | 900 | 1000 | 900 | 1500 | ppm |
Granularity | 8~10μm | 8~10μm | 7~9μm | 25μm | 25μm | 25μm | 25μm | 0.8mm | μm/mm |
Features
1. high temperature: Graphite is one of the most known high temperature materials. Its melting point is 3850°C±50°C and its boiling point is 4250°C. It is 10S under the 7000°C ultra-high temperature arc, the loss of graphite is minimal, and the loss of graphite is 0.8% by weight. It can be seen that the high temperature resistance of graphite plates is outstanding.
2. special thermal shock resistance: graphite has a good thermal shock resistance, that is, when the temperature changes abruptly, the thermal expansion coefficient is small, and thus has a good thermal stability, in the rapid change of temperature and heat, will not crack
3. thermal conductivity and conductivity: graphite has good thermal conductivity and conductivity. Compared with general materials, its thermal conductivity is quite high. It is 4 times higher than stainless steel, 2 times higher than carbon steel and 100 times higher than normal non-metal.
4. Lubricity: The lubricating property of graphite is similar to that of molybdenum disulfide, and the coefficient of friction is less than 0.1. Its lubricating properties vary with the size of the scales. The larger the scales, the smaller the coefficient of friction and the better the lubricity.
5. chemical stability: Graphite plate at room temperature h
as a good chemical stability, acid, alkali, resistant to organic solvent corrosion.